Microleakage evaluation of silorane based composite versus methacrylate based composite


Roula Al-Boni, Ola M Raja 
 Department of Operative Dentistry, School of Dentistry, Damascus University, Damascus, Syria

Correspondence Address:
Ola M Raja
Faiz Mansour St., Damascus University, Dentistry College, Damascus
Syria

Aim : Our study aimed to analyze the microleakage of silorane-based composite in comparison to two homologous methacrylate-based composites. Materials and Methods : Standardized class I cavities (4 × 2.5 × 3 mm) were prepared on extracted human premolars and randomly assigned into three groups (N = 15) as follows: Group A, Filtek P90 (silorane) with its dedicated adhesive system (P90 system adhesive); Group B, Adper SE Plus with Filtek Z250; Group C, Peak SE with Amelogen Plus. The teeth were subjected to thermocycling regime (200×, 5-55°C) and dye penetration of tooth sections were evaluated following 30 minute immersion in 2% Methylene Blue dye. Statistical analysis was performed with Kruskal-Wallis and Mann-Whitney U test at 95% significance level. Results : Silorane exhibited significantly decreased microleakage compared with any other resin based composite (RBC). The cavities restored with Amelogen Plus displayed nonsignificantly higher microleakage than with Filtek Z250. Conclusion : Although all of the restorative systems had microleakage, silorane technology showed less microleakage comparable to clinically successful methacrylate-based composite. This will improve the clinical performance and extend the composite durability.


How to cite this article:
Al-Boni R, Raja OM. Microleakage evaluation of silorane based composite versus methacrylate based composite.J Conserv Dent 2010;13:152-155


How to cite this URL:
Al-Boni R, Raja OM. Microleakage evaluation of silorane based composite versus methacrylate based composite. J Conserv Dent [serial online] 2010 [cited 2021 Oct 20 ];13:152-155
Available from: https://www.jcd.org.in/article.asp?issn=0972-0707;year=2010;volume=13;issue=3;spage=152;epage=155;aulast=Al-Boni;type=0