ORIGINAL RESEARCH ARTICLE  
Year : 2018  |  Volume : 21  |  Issue : 1  |  Page : 90-94
Scanning electron microscopic evaluation of marginal adaptation of AH-Plus, GuttaFlow, and RealSeal at apical one-third of root canals – Part II: Core-sealer interface


Department of Conservative Dentistry and Endodontics, Dr. R. Ahmed Dental College and Hospital, Kolkata, West Bengal, India

Click here for correspondence address and email

Date of Submission05-Apr-2017
Date of Decision15-Nov-2017
Date of Acceptance17-Dec-2017
Date of Web Publication19-Feb-2018
 

   Abstract 

Background: Not only the gaps at dentin-sealer interface but also at core-sealer interface may jeopardize the outcome of root canal treatment.
Aim: The aim of this in vitro scanning electron microscopic (SEM) study was to determine which root canal sealer among AH-Plus, GuttaFlow, and RealSeal provides a superior marginal adaptation with the core obturating material in the apical third region of root canals.
Materials and Methods: Selected 30 human freshly extracted maxillary central incisors were biomechanically prepared, then divided equally into three groups and obturated with AH-Plus, GuttaFlow, and RealSeal using single cone obturation technique. After sectioning longitudinally, apical third of the roots were observed under SEM dentin-sealer-core interface was focused. Marginal adaptation and interfacial gaps at core-sealer interface of all the samples were evaluated and analyzed statistically in this part of the article.
Statistical Analysis Used: Analysis of variance and post hoc Tukey's test.
Results: Mean average gap was significantly higher (P < 0.05) for AH-Plus (15.65 ± 10.48 μm), when compared to GuttaFlow (3.51 ± 1.81 μm) and RealSeal (6.01 ± 2.51 μm). Between RealSeal and GuttaFlow, the latter showed least marginal gap; however, this difference was not statistically significant (P > 0.05).
Conclusions: GuttaFlow is better adapted in the apical third of root canals among 3 sealers.

Keywords: AH-Plus; core-sealer interface; GuttaFlow; marginal adaptation; RealSeal; scanning electron microscope

How to cite this article:
Adhikari HD, Jain S. Scanning electron microscopic evaluation of marginal adaptation of AH-Plus, GuttaFlow, and RealSeal at apical one-third of root canals – Part II: Core-sealer interface. J Conserv Dent 2018;21:90-4

How to cite this URL:
Adhikari HD, Jain S. Scanning electron microscopic evaluation of marginal adaptation of AH-Plus, GuttaFlow, and RealSeal at apical one-third of root canals – Part II: Core-sealer interface. J Conserv Dent [serial online] 2018 [cited 2021 Dec 7];21:90-4. Available from: https://www.jcd.org.in/text.asp?2018/21/1/90/225737

   Introduction Top


Complete sealing of the root canal system after cleaning and shaping procedure is critical to prevent oral pathogens from colonizing and reinfecting the root and periapical tissues.[1] Marginal leakage could occur at the interface between the sealer-dentin as well as sealer-core obturating material.[2] In recent years, there has been continuous quest for such type of sealers that adhere simultaneously to canal wall dentin as well as core obturating materials, in an attempt to seal the root canal system more effectively. With this goal in mind, the purpose of present in vitro scanning electron microscopic (SEM) study is to determine which one of the commonly used root canal sealers among AH-Plus, GuttaFlow, and RealSeal provides a superior marginal adaptation both at dentin-sealer and core-sealer interface in the apical third region of root canals. Quality of seal along dentin-sealer interface has been evaluated quantitatively in Part I of this article whereas core-sealer interface has been focused here in this part.


   Materials and Methods Top


Thirty human maxillary central incisors, freshly extracted for periodontal cause, free from any open apices, cracks, calcified canals, canal curvature, and resorptive defects were selected for this study. Informed consent was obtained from the patients, and the Institutional Ethics Committee and Review Board gave ethical clearance for this study. Instrumentation was completed through crown-down technique with Profile ISO series rotary files until a size 40; 0.06 reached working length. Ethylenediaminetetraacetic acid was used as the final rinse before root canal obturation. Then, teeth were randomly divided into three experimental groups (Group I, II, III) of ten sample each.

All three endodontic sealers were mixed and used according to manufacturer's instructions and introduced into the canal space with master cone size 40;0.06. The teeth of Group I, Group II, and Group III were obturated with AH-Plus (Dentsply Maillefer, Ballaigues, Switzerland), GuttaFlow (Coltene Whaledent, DPI, Mumbai, Maharashtra, India), and RealSeal (SybronEndo, Orange, CA, USA) sealers, respectively, using mastercone gutta-percha in Group I and II and Resilon master cone in Group III. Single-cone obturation technique was employed.

The root canal opening of all three groups was then sealed with glass ionomer cement, and obturated teeth were stored at 37°C and 100% humidity for 7 days.

Each root was then longitudinally sectioned using a diamond disk on a slow speed handpiece to obtain the dentin-root canal filling interface at apical 3 mm of root. During sectioning, the specimens were subjected to continuous water cooling to prevent frictional heat, which minimizes smearing of core obturating materials that tend to hide areas of sealer as pointed by Vikram et al.[3] Apical third sections thus obtained were labeled accordingly.

All specimens were dehydrated in an ascending series of aqueous ethanol (70%, 80%, 90%, 95%, 100%), then gold sputtered and observed under SEM using high accelerating voltage of 15.0 kV at different magnifications ranging from ×25 to ×2000 to achieve a representative area containing both gap-containing and gap-free region and visualize a broader aspect of sample.

Under SEM, two-three representative areas from middle third of each sample were focused and core-sealer interfacial gaps were measured using ImageJ software [3] (Wayne Rasband; National Institute of Health, Bethesda, MA, USA). Overall average gaps at this interface were calculated for the each sample and were tabulated [Table 1].
Table 1: Analysis of core-sealer interfacial gap (μm)

Click here to view


Statistical analysis was performed with the help of Epi Info (TM) 3.5.3 (Centers for Disease Control and Prevention[CDC], Atlanta; Georgia [US]). EPI INFO is a trademark of the Centers for Disease Control and Prevention. One-way analysis of variance (ANOVA) followed by post hoc Tukey's test was performed with the help of critical difference (CD) or least significant difference at 5% and 1% level of significance to compare the mean values. P < 0.05 was taken to be statistically significant. To compare the means of 2 populations, t-test was used. P ≤ 0.05 was considered statistically significant.


   Results Top


  1. None of the groups showed complete marginal adaptation at core-sealer interface [Table 1] and [Figure 1]
  2. There were both gap-free and gap-containing regions at different levels in all groups. However, GuttaFlow exhibited better apical marginal adaptation with core obturating material [Figure 1]a and [Figure 1]b than RealSeal [Figure 1]c and [Figure 1]d and AH-Plus [Figure 1]e and [Figure 1]f At core-sealer interface, mean average gap was maximum for AH-Plus: 15.65 ± 10.48 μm, followed by RealSeal: 6.01 ± 2.51 μm and it was minimum for GuttaFlow which was 3.51 ± 1.81 μm [Table 1]. Statistical analysis ANOVA showed statistically significant difference among the three groups (P< 0.05) [Table 1]. Post hoc Tukey's test with the help of CD showed mean average gap of AH-Plus was significantly higher than that of GuttaFlow and RealSeal at 5% level of significance (P< 0.05); however, there was no significant difference between GuttaFlow and RealSeal (P > 0.05) [Table 1]
  3. When compared to dentin-sealer interface (as discussed in Part I), gap at core-sealer interface in AH-Plus group was significantly high (P< 0.05) [Figure 1]e and [Figure 1]f, whereas that in GuttaFlow and RealSeal group, no significant difference (P > 0.05) was seen [Table 2].
Figure 1: Scanning electron microscopic images: Core-Sealer interface – (a and b) GuttaFlow, good adaptation with minimal gap. (c and d) RealSeal, heterogeneous distribution with gaps at some places. (e and f) AH-Plus, wide gaps seen. D: Dentin, S: Sealer, C: Core

Click here to view
Table 2: Comparison of dentin-sealer and core-sealer interfacial gaps (μm)

Click here to view



   Discussion Top


Peripheral gaps along the dentin-sealer and core material-sealer interfaces may jeopardize the outcome of root canal treatment.[4] This part of the present study focused on comparative evaluation of marginal gap of AH-Plus, RealSeal, and GuttaFlow sealers at core-sealer interface using SEM. Marginal adaptation at the apical third region was assessed, as most critical area of prepared root canal is the apical 2–3 mm.[5]

Leakage studies using different methods to assess apical seal have shown conflicting results.[6],[7] Hence, the present study aimed to look at the core-sealer interface using SEM has larger depth of field, higher resolution, and better magnification at the interface which has been also pointed by Punithia and Shashikala.[8]

Single-cone obturation technique was employed as it is the most common method employed in clinical scenario and volume of the sealer was minimized because size and taper of gutta-percha and Resilon master cones were calibrated to the preparation size and taper.

In the present study, GuttaFlow (Group II) exhibited better adaptation [Figure 1]a and [Figure 1]b and least mean marginal gap at core-sealer interface compared to RealSeal and AH-Plus [Table 1]. The result of the present study (both Part I and Part II) that GuttaFlow shows better adaptation with both dentin and gutta-percha is also supported by the studies Vujasković and Teodorović,[9] Teodorović and Matović,[10] and Bouillaguet et al.[11] Better sealing ability of GuttaFlow is also found in other leakage studies.[12],[13]

This better adaptation of GuttaFlow to gutta-percha is mainly attributed to linear setting expansion of 0.16%,[14] following obturation in the canal and ability to flow into the canal.[12]

However, inferior sealing ability of GuttaFlow has also been found in the dye leakage [15] and glucose penetration model [16] studies. Such differences in performance may be attributed to the method used for evaluation and/or lateral compaction obturation technique employed in these studies.

In RealSeal (Group III), despite chemical bond between Resilon cone and RealSeal sealer, surprisingly mean average gap of 6.01 ± 2.51 μm occurred at core-sealer interface [Table 1], which could be possible due to the following reasons:

  1. The concentration of the polymeric components, polycaprolactone and urethane dimethacrylates is probably in the ratio of 10:1 in Resilon core, which may not be optimized for optimal adhesion of the root filling material to the methacrylate resin-based sealers [17],[18]
  2. Morphologic studies further revealed that the dimethacrylate in Resilon is not homogeneously dispersed within the polymer blend and appeared as phase separation components within the polycaprolactone [17],[19]
  3. As Resilon is used commercially as a fully polymerized material that lacks a free radical-containing oxygen inhibition layer, its bondability to resin-based sealers has further been questioned.[17]


All these above factors make bonding unpredictable at core-sealer interface.[20],[21] This is possibly reflected in SEM image [Figure 1]c and [Figure 1]d where sealer in some places is well adapted to Resilon whereas in some places, there is a gap. This heterogeneous distribution of the methacrylate resin-based sealer is also reported by Bouillaguet et al.[11]

AH-Plus (Group I), although had good adaptation at dentin-sealer interface [Table 2], showed significantly higher (P< 0.05) mean average gap at core-sealer interface compared to GuttaFlow and RealSeal. Greater gap at core-sealer interface [Figure 1]e and [Figure 1]f may be attributable to lack of bonding between AH-Plus and gutta-percha,[11],[22] and linear setting shrinkage of 0.034% ± 0.01% in AH-Plus.[23] Better adaptation between the dentin and AH-Plus but little adaptation between gutta-percha point and AH-Plus has been also seen in studies of Bouillaguet et al.[11] and Tay et al.[24]


   Conclusion Top


Under the parameters and limitations of the present study, it can be concluded that GuttaFlow is better adapted than RealSeal and AH-Plus to core obturating material as well as to dentin (discussed in Part I) in the apical third of root canals and thus may be the preferred sealer among the three to be used in clinical practice.

Nevertheless, results of this in vitro study need to be confirmed through further in vitro, in vivo, and ex vivo studies with large numbers of samples for longer period of time to arrive at a conclusion.

Limitation of the present study

  • There is a great risk that sectioning of the filled canal may result in tearing of the material or smearing of the gutta-percha and Resilon, that tend to hide areas of sealer
  • Examination of fully hydrated specimens by environmental SEM is essential for differentiating genuine gaps between root filling and dentin, from potential artifactual gaps created after vacuum desiccation in conventional SEM followed in this study.[24]


Acknowledgment

We would like to thank Indian Institute of Chemical Biology, Kolkata, for providing technical and instrumental support.

Financial support and sponsorship

Nil.

Conflicts of interest

There are no conflicts of interest.

 
   References Top

1.
Schilder H. Filling root canals in three dimensions. Dent Clin North Am 1967;11:723-44.  Back to cited text no. 1
    
2.
Hovland EJ, Dumsha TC. Leakage evaluation in vitro of the root canal sealer cement sealapex. Int Endod J 1985;18:179-82.  Back to cited text no. 2
    
3.
Vikram M, Shetty N, Singh VP. A comparative study to quantify the area of obturating material, sealer and voids in root canals obturated with resilon/epiphany and gutta-percha with different sealers. Nepal J Med Sci 2014;3:8-13.  Back to cited text no. 3
    
4.
Somma F, Cretella G, Carotenuto M, Pecci R, Bedini R, De Biasi M, et al. Quality of thermoplasticized and single point root fillings assessed by micro-computed tomography. Int Endod J 2011;44:362-9.  Back to cited text no. 4
    
5.
Gutmann JL, Fan B. Tooth morphology, isolation, and access. In: Hargreaves KM, editor. Cohen's Pathways of the Pulp. 11th ed. St. Louis: Elsevier; 2016. p. 142-4.  Back to cited text no. 5
    
6.
Wu MK, Wesselink PR. Endodontic leakage studies reconsidered. Part I. Methodology, application and relevance. Int Endod J 1993;26:37-43.  Back to cited text no. 6
    
7.
Ferreira R, Bombana AC, Sayeg IJ.In vitro analysis of the penetration of methylene blue dye in human radicular dentin using different methods of impregnation. Aust Endod J 2008;34:110-4.  Back to cited text no. 7
    
8.
Punithia PG, Shashikala K. Evaluation of the adaptation of resin based sealers epiphany, AH plus and AH 26 to the root canal dentin by scanning electron microscope. Indian J Stomatol 2011;2:207-11.  Back to cited text no. 8
    
9.
Vujasković M, Teodorović N. Analysis of sealing ability of root canal sealers using scanning electronic microscopy technique. Srp Arh Celok Lek 2010;138:694-8.  Back to cited text no. 9
    
10.
Teodorović N, Matović I. Scanning electron microscopic analysis of the sealing ability of GuttaFlow and Acroseal endodontic sealers. Stomatološki Glas Srb 2008;55:15-22.  Back to cited text no. 10
    
11.
Bouillaguet S, Shaw L, Barthelemy J, Krejci I, Wataha JC. Long-term sealing ability of pulp canal sealer, AH-plus, GuttaFlow and epiphany. Int Endod J 2008;41:219-26.  Back to cited text no. 11
    
12.
Nawal RR, Parande M, Sehgal R, Rao NR, Naik A. A comparative evaluation of 3 root canal filling systems. Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2011;111:387-93.  Back to cited text no. 12
    
13.
De-Deus G, Brandão MC, Fidel RA, Fidel SR. The sealing ability of GuttaFlow in oval-shaped canals: An ex vivo study using a polymicrobial leakage model. Int Endod J 2007;40:794-9.  Back to cited text no. 13
    
14.
Hammad M, Qualtrough A, Silikas N. Extended setting shrinkage behavior of endodontic sealers. J Endod 2008;34:90-3.  Back to cited text no. 14
    
15.
Rai K, Hegde MN, Hegde P. Apical sealing ability of newer resin based pulp space sealers – An in vitro study. Endodontology 2009;21:16-21.  Back to cited text no. 15
    
16.
Ozok AR, van der Sluis LW, Wu MK, Wesselink PR. Sealing ability of a new polydimethylsiloxane-based root canal filling material. J Endod 2008;34:204-7.  Back to cited text no. 16
    
17.
Hiraishi N, Papacchini F, Loushine RJ, Weller RN, Ferrari M, Pashley DH, et al. Shear bond strength of resilon to a methacrylate-based root canal sealer. Int Endod J 2005;38:753-63.  Back to cited text no. 17
    
18.
Tay FR, Hiraishi N, Pashley DH, Loushine RJ, Weller RN, Gillespie WT, et al. Bondability of resilon to a methacrylate-based root canal sealer. J Endod 2006;32:133-7.  Back to cited text no. 18
    
19.
Tay FR, Pashley DH, Williams MC, Raina R, Loushine RJ, Weller RN, et al. Susceptibility of a polycaprolactone-based root canal filling material to degradation. I. Alkaline hydrolysis. J Endod 2005;31:593-8.  Back to cited text no. 19
    
20.
Tay FR, Pashley DH. Monoblocks in root canals: A hypothetical or a tangible goal. J Endod 2007;33:391-8.  Back to cited text no. 20
    
21.
Schwartz RS. Adhesive dentistry and endodontics. Part 2: Bonding in the root canal system-the promise and the problems: A review. J Endod 2006;32:1125-34.  Back to cited text no. 21
    
22.
Teixeira CS, Alfredo E, Thomé LH, Gariba-Silva R, Silva-Sousa YT, Sousa-Neto MD, et al. Adhesion of an endodontic sealer to dentin and gutta-percha: Shear and push-out bond strength measurements and SEM analysis. J Appl Oral Sci 2009;17:129-35.  Back to cited text no. 22
    
23.
Zhou HM, Shen Y, Wang ZJ, Li L, Zheng YF, Häkkinen L, et al. In vitro cytotoxicity evaluation of a novel root repair material. J Endod 2013;39:478-83.  Back to cited text no. 23
    
24.
Tay FR, Loushine RJ, Weller RN, Kimbrough WF, Pashley DH, Mak YF, et al. Ultrastructural evaluation of the apical seal in roots filled with a polycaprolactone-based root canal filling material. J Endod 2005;31:514-9.  Back to cited text no. 24
    

Top
Correspondence Address:
Dr. Sakshi Jain
Dr. R. Ahmed Dental College and Hospital, 142/A, AJC Bose Road, New Building, 4th Floor, 2D PG, Kolkata - 700 014, West Bengal
India
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/JCD.JCD_127_17

Rights and Permissions


    Figures

  [Figure 1]
 
 
    Tables

  [Table 1], [Table 2]



 

Top
 
 
 
  Search
 
 
    Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
    Email Alert *
    Add to My List *
* Registration required (free)  
 


    Abstract
   Introduction
    Materials and Me...
   Results
   Discussion
   Conclusion
    References
    Article Figures
    Article Tables

 Article Access Statistics
    Viewed955    
    Printed21    
    Emailed0    
    PDF Downloaded117    
    Comments [Add]    

Recommend this journal