| Abstract|| |
Aim: To evaluate the shear bond strength of MTA with three different types of adhesive systems- self-adhering flowable composite, etch and rinse adhesive system and self etch adhesive system.
Methodology: MTA specimens (n = 60) were prepared using cylindrical acrylic blocks, having a central cavity with 4 mm diameter and 2 mm depth. MTA was mixed and placed in the prepared cavity, and was covered with a moist cotton pellet and temporary filling material. The specimens were divided into 3 groups which were further divided into 2 sub-groups (45 Minutes and 24 hours). After the application of bonding agents composite resin was placed over the MTA surface. The specimens were tested for shear bond strength and readings were statically analyzed.
Result: After 24 hrs the mean value of etch and rinse group was significantly higher than self etch and the self adhering composite groups. Among the 45 minutes groups there were no significant difference.
Conclusion: In single visit after 45 minutes self adhering flowable can be used successfully as a final restorative material in place of conventional flowable composite without using any alternative adhesive system over MTA.
Keywords: Etch and rinse (ER) adhesive; mineral trioxide aggregate (MTA); self-adhering flowable composite; self-etch (SE) adhesive
|How to cite this article:|
Tyagi N, Chaman C, Tyagi SP, Singh UP, Sharma A. The shear bond strength of MTA with three different types of adhesive systems: An in vitro study. J Conserv Dent 2016;19:130-3
|How to cite this URL:|
Tyagi N, Chaman C, Tyagi SP, Singh UP, Sharma A. The shear bond strength of MTA with three different types of adhesive systems: An in vitro study. J Conserv Dent [serial online] 2016 [cited 2020 Nov 26];19:130-3. Available from: https://www.jcd.org.in/text.asp?2016/19/2/130/178687
| Introduction|| |
Mineral trioxide aggregate (MTA) was introduced in 1993 and since then it has become a gold standard for many endodontic procedures. MTA is a biocompatible material , and has excellent sealing ability. It is claimed to provide double seal due to its physical sealing ability as well as ability to induce cementogenesis that provides biological seal. MTA has ability to set in the presence of moisture. Despite several advantages, prolonged setting time, and compulsion to place wet cotton pellet over MTA in some procedures to complete the setting reaction is a major drawback that necessitates second visit and increased chair time. 
Conventional glass ionomer cement (GIC) can be layered over partially set MTA after 45 min to complete the procedure in a single visit without any deleterious effect on either of the material. , Atabek et al. concluded that restorative procedure might be postponed at least for 96 h after mixing MTA to allow the material to achieve its optimum physical properties. 
Some studies also suggested that composite resin with a bonding agent can be restored over MTA almost immediately after the placement of MTA. When hydration during MTA setting process is guaranteed, there are no particular problems related to composite resin restoration even if it is performed almost immediately after MTA filling.  However, acid etching before composite placement reduces the compressive strength and surface microhardness of MTA. Kayhan et al. observed that acid etching created surface changes that might have potential to enhance bonding of resinous materials.  The nature of the solvent (acetone, ethanol, or water) and the filler content of the adhesive may also influence the bond strength of MTA to resin. 
Dyad flow, a new generation flowable composite, is recently introduced in restorative dentistry; this self-adhering composite is designed to bond to tooth structure without the need for a separate adhesive or an etching step.  The reduction in the number of steps can lead to lesser chances of procedural errors and lesser chair side time and results in more patient comfort during placement and hence are less technique sensitive than total etch and self-etch (SE) adhesives.  The bonding mechanism of self-adhering composite relies on a monomer glycerol phosphate dimethacrylate (GPDM) adhesive. Dyad flow bonds in two ways as follows: Primarily, through the chemical bond between the phosphate functional groups of a GPDM monomer and calcium ions of the tooth and, secondarily, through a micromechanical bond as a result of an interpenetrating network formed between the polymerized monomers of dyad flow and collagen fibers of dentin. 
Studies evaluating the physical properties, bond strengths, and marginal leakage of self-adhering composite to tooth have been reported, but no study has compared the bond strength of self-adhering composite with SE and etch and rinse (ER) adhesive systems when placed over MTA. The aim of this study is to evaluate the shear bond strength of MTA with three different types of adhesive systems, a self-adhering flowable composite, a SE adhesive system, and an ER adhesive system.
| Materials and methods|| |
The materials used in this study were tested and applied as recommended by the manufacturers. The materials used are listed in [Table 1].
Preparation of MTA specimens
Sixty MTA specimens were prepared by using cylindrical acrylic blocks. Each block had a central cavity measuring 4 mm in diameter and 2 mm in depth. The MTA was mixed according to the manufacturer's instructions, placed into the central cavity in the acrylic blocks, and covered with a moist cotton pellet and temporary filling material (Cavit; 3M ESPE America, Norristown, PA). Half of the specimens were stored for 45 min, and the remaining 30 specimens were stored for 24 h at 37°C temperature and 100% humidity.
After removing the temporary material and moist cotton, the MTA surface was not rinsed or polished. Sixty samples were divided into three groups according to the type of adhesive system used and these groups were further divided into two subgroups (N = 10) according to the different time intervals. The divisions of groups are listed in [Table 2].
|Table 2: Different groups at different time intervals for bond strength test|
Click here to view
In the SE and ER groups, the corresponding adhesive system was applied over MTA according to the manufacturer's instruction following which a conventional flowable composite Brilliant Flow (Coltene Whaledent, Switzerland) was placed over MTA surface with the help of cylindrical plastic tube having an internal diameter of 2 mm and a height of 3 mm. Light curing was done with a quartz-tungsten-halogen (QTH) light curing unit (Spectrum 800, DENTSPLY Caulk Milford, DE, USA) at an intensity of 600 mW/cm 2 for 20 s.
In the DF Group, the self-adhering composite was placed over MTA in increments. A layer of 1.5 mm was first placed inside the cylindrical plastic tube and agitated over the MTA surface with the help of an application brush. Light curing was done using a QTH light curing unit (Spectrum 800, DENTSPLY Caulk Milford, DE, USA) at an intensity of 600 mW/cm 2 for 20 s and then the remaining height of the plastic tube was filled in the second pour and light curing was done.
The plastic tubes were removed carefully and the specimens were stored at 37°C temperature and 100% humidity for 24 h to encourage setting.
Shear bond strength measurement
The specimens were mounted in a universal testing machine (Instron Corp, Canton, MA). A crosshead speed of 0.5 mm/min was applied to each specimen by using a knife-edge blade until the bond between the MTA and composite failed. The values were calculated in newtons and converted into megapascals (MPa) by using formula 4 × F/ðd 2 . Here, "F0" is the force in newton and "d" is the diameter of composite block. The means and standard deviations were calculated. The mean bond strengths of the groups were compared by using one-way analysis of variance (ANOVA) and Tukey's post hoc test (significance level, P < .05).
| Results|| |
The means and standard deviations of the shear bond strengths are given in [Table 3]. There was no significant difference between dyad flow and SE groups at both the time intervals. However, there is a significant difference between the mean bond strengths at 45 min and 24 h for the ER group, when compared with SE and dyad flow groups.
| Discussion|| |
MTA have been used successfully as a material for use in perforation repair and retrograde filling and eventually, it was recommended for pulp capping, pulpotomy, and as an apical barrier in the treatment of immature teeth with nonvital pulps and open apices as pulp capping agents in vital pulp therapy. , Following pulp capping, direct resin composites can be used for final restoration.  However, the use of SE adhesive or etching procedure over MTA surface has been reported to reduce microhardness, with the selective loss of matrix from around the crystalline structures on the MTA surface. Investigators have recommended that the application of ER and SE adhesive over MTA be postponed for 96 h  and that low condensation forces be used for coronal restoration over MTA  because of the material's low initial compressive strength. Flowable composite can be used without compression forces, and the new FC (dyad flow) does not require surface pretreatment before bonding because it acts as both an adhesive and a composite. 
The most common method to evaluate adhesive properties of restorative materials is bond strength assessment. This has become a well recognized method to analyze an important part of the in vitro performance of materials.  So the shear bond strength test has been used in this study to evaluate the adhesive properties of MTA with a self-adhering composite (dyad flow), a SE adhesive, and an ER adhesive. The mean bond strength of dyad flow, -SE, and ER groups is lesser at 45 min in comparison with 24 h interval and statistically there is no significant difference between dyad flow, SE and ER groups at 45 min (P = 0.875, 0.753, and 0.943, respectively). However, there is a significant difference between the mean bond strengths at 45 min and 24 h for the ER group, when compared with SE and dyad flow groups whereas there is no significant difference in the mean bond strengths between the dyad flow and SE groups at 24 h. (at 45 min P = 0.038 and at 24 h P = 0.001).
Recent studies evaluating the bond strength of adhesives to MTA, using various bonding systems, concluded that superior MTA-composite bond strength can be achieved with an ER adhesives at 24 h in comparison to SE system. ,
SE adhesives are gaining popularity because of simplified bonding procedures and reduced technique sensitivity. The SE approach uses acidic adhesive monomers that simultaneously demineralize and infiltrate into the dentin. The intensity of the interaction of SE adhesive systems with dentin was mostly dependent on the acidity and aggressiveness of the primer used.  SE adhesives have been classified based on their ability to penetrate smear layers and depth of demineralization as ultra-mild (pH >2.5), mild (pH ~2), moderately strong (pH 1-2), and strong (pH ≤1). The manufacturer of dyad flow has declared that it has a pH of 1.9, and One Coat 7.0 (Coltene Whaledent, Switzerland), a mild SE adhesive, has a reported pH of 2.0. Thus, dyad flow can be expected to interact with the dental substrate in a manner similar to that of a mild SE adhesive.  The results of this study showed that there is no significant difference between the bond strength of dyad flow, SE adhesive, and ER adhesive after 45 min. However, the bond strength of the composite to MTA was significantly higher for the ER group after 24 h.
Previous studies have evaluated the bond strengths of adhesives to MTA using various bonding system. Although acid etching reduces the surface microhardness of MTA and weakens the structure of the material, the results of these studies have shown that superior MTA/composite bond strength can be achieved with ER adhesives in comparison with one-step SE systems.  Phosphoric acid etching significantly enhances the surface energy of the substrate, thereby provides significantly more microretention and potentially increases the bonding effectiveness of resinous materials.  However, according to this study, there is no significance difference between dyad flow, -SE, and ER group at 45 min. The mild etching efficacy of dyad flow (pH 1.9) in comparison to aggressive phosphoric acid in ER group might be a reason for lower bond strength value at 24 h. Dyad flow and SE adhesive have pH of 1.9 and 2.0, respectively, and due to similar etching effectiveness the bond strength values are almost same.
| Conclusion|| |
Within the limitation of this in vitro study, it can be concluded that there is no significant difference in the mean bond strength values for dyad flow, - SE, and ER groups at 45 min. However, there is a significant difference in the mean bond strength values for ER adhesives when compared to dyad flow and SE adhesives at 24 h. Thus, to complete the clinical procedure in a single visit and to reduce the clinical steps, dyad flow can be used as an alternative to SE or ER adhesives as a definitive restoration after 45 min.
Financial support and sponsorship
Conflicts of interest
There are no conflicts of interest.
| References|| |
Keiser K, Johnson CC, Tipton DA. Cytotoxicity of mineral trioxide aggregate using human periodontal ligament fibroblasts. J Endod 2000;26:288-91.
Ribeiro DA, Matsumoto MA, Duarte MA, Marques ME, Salvadori DM. Ex vivo
biocompatibility tests of regular and white forms of mineral trioxide aggregate. Int Endod J 2006;39:26-30.
Torabinejad M. Clinical applications of mineral trioxide aggregate. Alpha Omegan 2004;97:23-31.
Nandini S, Ballal S, Kandaswamy D. Influence of glass-ionomer cement on the interface and setting reaction of mineral trioxide aggregate when used as a furcal repair material using laser Raman spectroscopic analysis. J Endod 2007;33:167-72.
Ballal S, Venkateshbabu N, Nandini S, Kandaswamy D. An in vitro
study to assess the setting and surface crazing of conventional glass ionomer cement when layered over partially set mineral trioxide aggregate. J Endod 2008;34:478-80.
Didem Atabek D, Sillelioðlu H, Olmez A. Bond strength of adhesive systems to mineral trioxide aggregate with different time intervals. J Endod 2012;38:1288-92.
Tsujimoto M, Tsujimoto Y, Ookubo A, Shiraishi T, Watanabe I, Yamada S, et al
. Timing for composite resin placement on mineral trioxide aggregate. J Endod 2013;39:1167-70.
Kayahan MB, Nekoofar MH, Kazandað M, Canpolat C, Malkondu O, Kaptan F, et al
. Effect of acid-etching procedure on selected physical properties of mineral trioxide aggregate. Int Endod J 2009;42:1004-14.
Yesilyurt C, Ceyhanli K, Kedici Alp C, Yildirim T, Tasdemir T. In vitro
bonding effectiveness of new self-adhering flowable composite to calcium silicate-based material. Dent Mater J 2014;33:319-24.
Motayam KE, Fouad WA, Youssef R. Assessment and comparison of nanoleakage and resin tag length of three different pit and fissure sealants: An in-vitro
scanning electron microscope study. Journal of American Science 2013;9:329-37.
Aman N, Khan FR, Salim A, Farid H. A randomized control clinical trial of fissure sealant retention: Self etch adhesive versus total etch adhesive. J Conserv Dent 2015;18:20-4.
Camilleri J, Montesin FE, Brady K, Sweeney R, Curtis RV, Ford TR. The constitution of mineral trioxide aggregate. Dent Mater 2005;21:297-303.
Accorinte ML, Loguercio AD, Reis A, Bauer JR, Grande RH, Murata SS, et al
. Evaluation of two mineral trioxide aggregate compounds as pulp-capping agents in human teeth. Int Endod J 2009;42:122-8.
Bayrak S, Tunç ES, Saroðlu I, Eðilmez T. Shear bond strengths of different adhesive systems to white mineral trioxide aggregate. Dent Mater J 2009;28:62-7.
Hashem AA, Wanees Amin SA. The effect of acidity on dislodgment resistance of mineral trioxide aggregate and bioaggregate in furcation perforations: An in vitro
comparative study. J Endod 2012;38:245-9.
Sirisha K, Rambabu T, Ravishankar Y, Ravikumar P. Validity of bond strength tests: A critical review-Part II. J Conserv Dent 2014;17:420-6.
Nasreen F, Guptha AS, Srinivasan R, Chandrappa MM, Bhandary S, Junjanna P. An in vitro
evaluation of effect of eugenol exposure time on the shear bond strength of two-step and one-step self-etching adhesives to dentin. J Conserv Dent 2014;17:280-4.
Vichi A, Margvelashvili M, Goracci C, Papacchini F, Ferrari M. Bonding and sealing ability of a new self-adhering flowable composite resin in class I restorations. Clin Oral Investig 2013;17:1497-506.
Department of Conservative Dentistry and Endodontics, Kothiwal Dental College and Research Centre, Moradabad, Uttar Pradesh
Source of Support: None, Conflict of Interest: None
[Table 1], [Table 2], [Table 3]