| Abstract|| |
Aim and Objectives: This in vitro study was designed to comparatively evaluate the effect of five commercial mouth rinses on the micro hardness of a nanofilled resin based restorative material.
Materials and Methods: Fifty specimens of resin composite material (Filtek Z350XT, 3M ESPE, St.Paul, MN USA) were prepared and immersed in artificial saliva for 24 h. The base line micro hardness of specimens was recorded using Vicker's micro hardness tester (MMT - X7 Matsuzawa, Japan). The specimens were randomly distributed into five groups, each containing 10 specimens (n=10) as follows - Group I Listerine (alcohol based), Group II Periogard (alcohol based), Group III Colgate plax (alcohol based), Group IV C- prev (alcohol free), Group V Hiora(alcohol free). The specimens were immersed in 20 ml of mouth rinses and incubated for 24 h at 37°C. The post immersion micro hardness values of the specimens were recorded and the data was tabulated for statistical analysis. Kruskal-Wallis test was used for inter group comparison followed by pair wise comparison of groups using Mann-Whitney U test. The level of significance was set at P=0.05.
Results: Significant reduction in the mean VHN (Vicker's micro hardness number) was observed in all the groups after exposure to the tested mouth rinses (P<0.01) and the reduction in mean VHN values were as follows: Group I 12.09, Group II 3.42, Group II 1.51, Group IV 1.03, Group V 0.57. Inter group comparison showed statistically significant reduction in micro hardness in Groups I and II compared to all other groups with P<0.001. There was no significant difference between Groups III, IV and V.
Conclusion: All the mouth rinses showed a reduction in the microhardness of nanofilled resin composite material with listerine (Group I) containing maximum amount of alcohol, showing highest reduction in micro hardness value.
Keywords: Resin composite; mouth rinse; microhardness
|How to cite this article:|
Jyothi K N, Crasta S, Venugopal P. Effect of five commercial mouth rinses on the microhardness of a nanofilled resin composite restorative material: An in vitro study. J Conserv Dent 2012;15:214-7
|How to cite this URL:|
Jyothi K N, Crasta S, Venugopal P. Effect of five commercial mouth rinses on the microhardness of a nanofilled resin composite restorative material: An in vitro study. J Conserv Dent [serial online] 2012 [cited 2020 Oct 25];15:214-7. Available from: https://www.jcd.org.in/text.asp?2012/15/3/214/97938
| Introduction|| |
Mouth rinses are widely used to prevent and control caries and periodontal diseases, with some individuals using mouth rinses at a frequency of six times per day.  Mouth rinses contain water, antimicrobial agents, salts, preservatives and in some cases alcohol. The variation in the concentration of these substances affects the pH of mouth rinses. 
Alcohol in the mouth rinses may soften the resin composite restorative materials  and this effect is found to be directly related to the percentage of alcohol.  Low pH increases sorption, solubility and surface degradation of resin composites.  The type of restorative material also influences the degradation of restorative materials. ,,,,,
The use of nanofilled resin composites has become popular in recent years because of their esthetics and good mechanical properties. ,,, Currently a wide variety of mouth rinses are available in the market and many of them are not studied for their effect on the restorations. Hence the aim of the study was to comparatively evaluate the effect of five commercial mouth rinses on the micro hardness of a nanofilled resin composite (Filtek Z350 XT, 3M ESPE, St. Paul, MN, USA).
| Materials and Methods|| |
The details of the commercial mouth rinses and the tested resin composite are shown in [Table 1] and [Table 2].
|Table 1: Composition, pH and group allocation of mouth rinses used in the study|
Click here to view
|Table 2: Product profile of nano filled resin composite used in the study|
Click here to view
Fifty specimens of nanofilled resin based composite material with 3 mm in diameter and 3 mm in height were prepared using a plastic mold which was custom modified to get the desired size. The mold was placed on a glass slide(Microglass industries,pahari Dhiraj,Delhi) and filled with resin composite to a slight excess using composite filling instrument (GDC Marketing co, Hoshiarpur, India) covered with a clear matrix strip (Samit products, Jandewalan, New Delhi) and another glass slide was placed on top and gently pressed for 30 s to extrude excess material to obtain a smooth surface. Each specimen was cured for 40 s from the top and another 40 s from the bottom using LED light cure unit (Blue phase C8, Ivoclar Vivadent, Astria) at 800 mW/cm 2 . The specimens thus prepared were kept in artificial saliva for 24 h to simulate the oral environment.
The pH of five commercial mouth rinses was recorded using a digital pH meter (servewell instruments and equipments Pvt. Ltd, Bangalore). The values are entered in [Table 1].
Micro hardness testing
The specimens were randomly divided into five groups of 10 specimens each (n=10) as follows: Group I Listerine (alcohol based), Group II Periogard (alcohol based), Group III Colgate plax (alcohol based), Group IV C- Prev (alcohol free, fluoride containing), Group V Hiora (alcohol free, herbal). The baseline micro hardness values of the specimens were recorded using Vicker's micro hardness tester (MMT - X7 Matsuzuwa, Japan) with a load of 200 g and a dwell time of 15 s.
The specimens were then immersed in 20 ml of respective mouth rinses and kept in an incubator at 37°C for 24 h. The specimens were then checked for post immersion micro hardness using the same micro hardness tester previously mentioned for base line values. The data was tabulated and subjected to statistical analysis.
The intra group (pre and post immersion values) comparison of the mean value of micro hardness of the specimens was done using Wilcoxon signed rank test. For inter group comparison Kruskal-Wallis test followed by Mann-Whitney U test was used with SPSS version 16 (SPSS Inc.,Chicago) and micro soft excel version 7 (Micro soft corporation NY, USA). The level of significance was set at P=0.05.
| Results|| |
Significant reduction in the micro hardness was observed in all the groups after immersion in the mouth rinses compared to baseline values with P<0.01.
Kruskal-Wallis test showed a statistically significant difference in micro hardness between the five groups of mouth rinses with P< 0.05. Further analysis was done applying Mann-Whitney U test for pair wise comparison.
Group I (Listerine) and Group II (Periogard) showed significant reduction in the micro hardness compared to Group III (Colgate plax), IV(C- Prev) and V(Hiora) with P>0.001, whereas there was no statistically significant difference between Groups III and IV (P=0.8), Groups III and V (P=0.48) and Groups IV and V (P=0.19) as shown in [Table 3].
|Table 3: Intra (row) and inter (column) group comparison of microhardness (mean VHN) in various mouth rinses|
Click here to view
| Discussion|| |
The present in vitro study was designed to comparatively evaluate the effect of mouth rinses on the micro hardness of a nanofilled resin composite Filtek Z350 XT. Listerine, Periogard and Colgate Plax are alcohol-based mouth rinses. C-Prev and Hiora are alcohol-free mouth rinses. The study design is an "active arm controlled trial" which does not require a parallel placebo arm. Hence there is no control group included in the study.
Hardness is considered as the test parameter, as it is an important property for the restorative materials to have long-term durability in the oral cavity.  Hardness may be defined as the resistance of a material to indentation or penetration.  Strength, proportional limit and ductility are related to hardness. Hardness has also been used to predict the wear resistance of a material and its ability to abrade or be abraded by opposing dental structures and materials.  So a decrease in the hardness of a material may result in premature failure of a restoration requiring its replacement.
In the present study, all the mouth rinses irrespective of the presence or absence of alcohol resulted in significant reduction in the micro hardness of the tested nanofilled resin composite material compared to base line values. This may be because of the acidic pH of the mouth rinses which would have caused acid erosion of the resin composite by acid etching and leaching the principle matrix forming cations. This is in accordance with the observations by Dieb et al in 2007  who reported that mouth rinses with low pH are detrimental to the hardness of resin composites. Basically the low pH of mouth rinses may have acted in the polymeric matrix of the nanofilled resin composite used in the study, through catalysis of ester groups from dimethacrylate monomers present in the composition (Bis GMA, Bis EMA, UDMA and TEG DMA).  The hydrolysis of these ester groups may have formed alcohol and carboxylic acid molecules that may have accelerated the degradation of the resin composite. 
Inter group comparison showed Listerine (Gr. I) and Periogard (Gr. II), containing alcohol 21.6% w/v and 11.6 % w/v respectively, resulting in statistically more reduction in the micro hardness compared to Grs. III, IV and V. Colgate plax (Gr. III) although contains alcohol (7.2% v/v) did not show statistically significant difference compared to C-Prev (Gr. IV) and Hiora (Gr. V) which are alcohol free. This may be because of the lower percentage of alcohol in Colgate plax. This observation is in accordance with the observations by Penugonda et al who reported that the higher percentage of alcohol in the mouth rinses causes more reduction in the hardness of restorative materials.
The softening effect of alcohol in the mouth rinses on the resin composite may be due to susceptibility of Bis GMA and UDMA based polymers present in them  and irreversible leaching of the components.  This effect may be more pronounced in nanofilled resin composites according to the observation by Karabela et al and Almeida GS et al who showed higher sorption rate for nanofilled resin composites in ethanol/water than in water or saliva. The reasons for this may be -
As observed in the study, alcohol content and low pH can have an effect on the micro hardness, but these two factors may not be interdependent on each other in reducing the micro hardness of the resin composite tested. Though Hiora has low pH than Periogard, it shows less reduction in micro hardness than Periogard, may be because it has no alcohol in it.
- Greater surface area to volume ratio derived from the non agglomerated 20 nm silica filler.
- Poor impregnation of 5 to 20 nm sized primary particles by the polymeric matrix.
Hence the long-term, regular use of alcohol based mouth rinses like Listerine and Periogard with higher alcohol content (21.6% w/v and 11.6% w/v respectively) and low pH may be detrimental to the nanofilled resin composite used in the present study. However the results of this in vitro study may not be directly related to the clinical situation where saliva may dilute or buffer the mouth rinses. Hence further in vivo studies are recommended.
| Conclusions|| |
Within the limitations of the experimental design and the test parameter, it can be concluded that -
- Listerine mouth rinse containing highest amount of alcohol showed maximum reduction in micro hardness of nanofilled resin composite Filtek Z350 XT.
- All the mouth rinses used in the study irrespective of the presence or absence of alcohol reduced the micro hardness of nanofilled resin composite.
| References|| |
|1.||Moran JM. Chemical plaque control prevention for the masses. Periodontology 2000;15:109-17. |
|2.||Bhatti SA, Walsh TF, Douglas CW. Ethanol and pH levels of proprietary mouth rinses. Community Dent Health 1994;11:71-4. |
|3.||Asmussen E. Softening of BIS GMA based polymers by ethanol and by organic acids of plaque. Scand J Dent Res 1984;92:257-61. |
|4.||Penugonda B, Settembrini L, Scherer W, Hittel E, Strassler H. Alcohol containing mouth washes: Effects on composite hardness. J Clin Dent 1994;5:60-2. |
|5.||Almeida GS, Poskus LT, Guimaraes JG, Da silva EM. Effect of mouth rinses on salivary sorption, solubility and surface degradation of a nano filled and a hybrid resin composite. Oper Dent 2010;35:105-11. |
|6.||Indrani DJ, Triaminingsih S, Nurvanita LN, Yulanti AN. Effect of ethanol in mouth rinses on the surface hardness of a dental resin composite material. Padjadjaran J Dent 2009;21:8-13. |
|7.||Diab M, Zaazou MH, Mubarak EH, Olaa MI Fahmy. Effect of five commercial mouth rinses on the micro hardness and color stability of two resin composite restorative materials. Aust J Basic Appl Sci 2007;1:667-4. |
|8.||Miranda DA, Bertoldo CE, Baggio Aguiar FH, Leite Lima DA, Lovandino JR. Effects of mouth washes on knoop hardness and surface roughness of dental composites after different immersion times. Braz Oral Res 2011;25:168-73. |
|9.||Ateyah NZ. The effect of different mouth rinses on micro hardness of tooth cocoured restorative materials. J Pak Dent Assoc 2005;14:150-3. |
|10.||Gurgan S, Oner A, Koprulu H. In vitro effects of alcohol containing and alcohol free mouth rinses on micro hardness of some restorative materials. J Oral Rehab 1997;24:244-6. |
|11.||Yap AU, Tan BW, Tay LC, Chang KM, Loy TK, Mok BY. Effect of mouth rinses on micro hardness and wear of composite and compomer restoratives. Oper Dent 2003;28:740-6. |
|12.||Mozner N, Klapohr S. nanotechnology for dental composites. Int J Nanotechnol 2004;1:130-41. |
|13.||Swift EJ. Nanocomposites. J Esthet Dent 2006;17:3-4. |
|14.||Hegde MN, Hegde P, Bhandary S, Deepika K. An evaluation of compressive strength of newer nanocomposite: An in vitro study. J Conservative dent 2011;14:36-9. |
|15.||Gogna R, Jagadish S, Shashikala K. A comparative in vitro study of microleakage by a radioactive isotope and compressive strength of three nanofilled composite resin restorations. J Conserv Dent 2011;14:128-31. |
|16.||Okada K, Tosaki S, Hirota K, Hume WR. Surface hardness change of restorative filling materials in saliva. Dent Mater 2001;17:34-9. |
|17.||O'Brien WJ. Physical properties of dental materials and their selection. Illinois: Quintessence Publishing Company; 1977. p. 18. |
|18.||Anusavice KL. Mechanical properties of dental materials in phillip's science of dental materials. 10 th ed. Philadelphia: WB Saunder's Co.; 1996. p. 69. |
|19.||Dental manufacturers/products/dental restorative materials/dental composites/dental-nanocomposites/#tab2. Available from: htpp//solutions.3mae.ae/wps/portal/3M/en-AE/3M-ESPE [Last accessed on 2011 Sep 20]. |
|20.||Gopferich A. Mechanisma of polymer degradation and erosion. Biomaterials 1996;17:103-14. |
|21.||Kao EC. Influence of food stimulating solvents on resin composites and glass ionomer restorative cement. Dent Mater 1989;5:201-8. |
|22.||Lee SY, Geener EH, Menis DL. Detection of leached moieties from dental composites in fluid simulating food and saliva. Dent Mater 2000;16:33- 40. |
|23.||Karabela MM, Sideridou ID. Effect of the structure of silane coupling agent on sorption charecteristics of solvents by dental resin composites. Dent Mater 2008;24:1631-9. |
K N Jyothi
# 101, 2nd Cross, 4th Main, Incometax Layout, Near Attiguppe, Vijaynagar, Bangalore - 560 040, Karnataka
Source of Support: None, Conflict of Interest: None
[Table 1], [Table 2], [Table 3]