Journal of Conservative Dentistry

ORIGINAL ARTICLE
Year
: 2014  |  Volume : 17  |  Issue : 3  |  Page : 230--233

An in vitro comparative evaluation of physical properties of four different types of core materials


Antara Agrawal, Kundabala Mala 
 Department of Conservative Dentistry and Endodontics, Manipal College of Dental Sciences, Manipal University, Mangalore, Karnataka, India

Correspondence Address:
Kundabala Mala
Department of Conservative Dentistry and Endodontics, Manipal College of Dental Sciences, Manipal University, Mangalore - 576 104, Karnataka
India

Abstract

Introduction: Compressive and tensile stresses of core materials are important properties because cores usually replace a large bulk of tooth structure and must resist multidirectional masticatory forces for many years. Material and Methods: The present study was undertaken to find out the best core build up material with respect to their physical properties among resin-based composites. Individual compressive, tensile, and flexural strength of fiber-reinforced dual cure resin core build up material, silorane-based composite resin, and dual curing composite for core build up with silver amalgam core was used as control were evaluated and compared using universal testing machine. Data were statistical analysed using Kruskal-Wallis test to determine whether statistically significant differences (P < 0.05) existed among core materials. Both dual cure composite materials with nanofillers were found superior to amalgam core. The silorane-based material showed the highest flexural strength, but other mechanical properties were inferior to dual cure composite materials with nanofillers.



How to cite this article:
Agrawal A, Mala K. An in vitro comparative evaluation of physical properties of four different types of core materials.J Conserv Dent 2014;17:230-233


How to cite this URL:
Agrawal A, Mala K. An in vitro comparative evaluation of physical properties of four different types of core materials. J Conserv Dent [serial online] 2014 [cited 2019 Sep 21 ];17:230-233
Available from: http://www.jcd.org.in/text.asp?2014/17/3/230/131782


Full Text

 INTRODUCTION



The restoration of endodontically treated teeth offers many challenges for the restorative dentist because of the large percentage of failures and this high incidence of failure has led to the development of a magnitude of restorative alternatives for endodontically treated teeth. [1] A foundation restoration or core is used to build a badly broken down tooth to restore the bulk of the coronal portion of the tooth to an ideal anatomic form before the full coverage crown is placed. It should provide the patient a long-lasting restoration with adequate function. Subsequent tooth preparation is greatly simplified if the tooth is built up to an ideal contour. [2] Because the core becomes an integral part of the structure of the tooth, it should provide strength to resist intraoral compressive and tensile forces. [3]

Compressive and tensile stresses of core materials are thought to be important because cores usually replace a large bulk of tooth structure and must resist multidirectional masticatory forces for many years. [4],[5],[6] Flexural strength of core materials is considered to be sensitive to surface imperfections such as cracks, voids, and related flaws, which can influence the fracture strength of brittle materials. [7]

Development and advances in non-gamma-2 amalgams and the new concepts of bonding dental amalgam to tooth structure have helped to ensure that amalgam remains one of the material widely used for core build up procedures in posterior teeth. [8],[9] However, this material has disadvantages like poor color, low-initial strength, lack of inherent bond to tooth structure, and high coefficient of thermal diffusibility. Patients are increasingly requesting biocompatible metal-free restorative systems, which are readily available in the market. [10],[11]

When considering resin-based composites, one should keep in mind that this in fact represents a composite family consisting of, particulate filler composites and fiber-reinforced composites, being the subject of the present study. [12]

LuxaCore dual (DMG, Germany) can be automatically mixed and dispensed with intraoral tips, has ideal flow properties allowing tooth substance, and posts to be totally surrounded, while avoiding gaps or air pockets and is available in different shades. LuxaCore dual (DMG) not only possesses similar strength, flexibility, and insulation properties to that of dentin but it also cuts and trims like dentin and is not too hard as many other core or general restorative composites tend to be. It has thorough and even distribution of nanoparticles throughout the resin matrix, resulting the virtual elimination of particle agglomeration. [13]

ParaPost ParaCore Automix 5 ml (Coltene Whaledent, USA) is a fiber-reinforced, dual core, and radiopaque core build up material. It exhibits a stackable, non-slumping consistency and is formulated to cut similar to dentin, allowing the bur to move smoothly between natural tooth structure and the material without creating troughs and grooves. It incorporates glass particles that impart high strength. [14]

Despite innovative improvements during the years and the excellent acceptance of methacrylate-based restorative materials, polymerization shrinkage stress is still considered as being their main drawback. [15] Several in vitro studies found a significant correlation between marginal adaptation of dental composites or microleakage and reduced shrinkage stress. [16],[17],[18]

One of this new low-polymerization shrinkage materials currently introduced in the European market is based on innovative monomer system - silorane - obtained from the reaction of oxirane and siloxane molecules. [19] The novel resin is considered to have combined the two key advantages of the individual components: low-polymerization shrinkage due to the ring opening oxirane monomer and increased hydrophobicity due to the presence of the silorane species. The mechanism of compensating stress in this new system is achieved by the opening of the oxirane ring during polymerization. [20] FiltekTM P90 is the first composite to shrink less than 1% with low-shrinkage posterior restorative system based on 3M ESPE's latest product innovation: silorane chemistry. It combines the lowest shrinkage silorane-based composites with a dedicated two step self-etching bonding system. This silorane-based composite shows the lowest volumetric shrinkage to date. It has excellent marginal integrity, easy to handle, non-sticky, and excellent ability to hold shape. It is strong, durable and has low water sorption for substantially decreased exogenic staining. [21]

Hence, the present study was undertaken to find out the best core build up material with respect to their physical properties among resin-based composites.

Objectives were

To evaluate and to compare the individual compressive, tensile, and flexural strength of fiber-reinforced dual cure resin core build up material (ParaCore, Coltene Whaledent), silorane-based composite resin (P-90 FiltekTM) and dual curing composite for core build up (Luxacore, DMG,Germany) with silver amalgam core was used as control.

 MATERIALS AND METHODS



All the four core build up materials were manipulated according to manufacturers' instructions.Cylindrical specimens measuring 6-mm high and 4 mm in diameter were made in Teflon and aluminium molds, covered with polyethylene strips and held within clamps for 30 s at room temperature (23 ± 10°C) and relative humidity of 50 ± 5%. Photopolymerization was initiated by illuminating two surfaces of the specimen for 40 s. When the specimen's height was greater than 3 mm, the samples were taken out of molds and illuminated for 40 additional seconds to ensure a good polymerization depth. The samples were then left to set in the molds at room temperature for 10 min before being stored at 37°C in a humid environment. All properties were measured at end of 24 hrs. The dimensions of the samples were measured by use of a vernier caliper. Test specimens were mounted vertically between disks of blotting paper on the platens of a universal testing machine (Instron Machine 3366, made in USA). Specimens were loaded at a cross-head speed of 0.5 mm/min. Failure load was recorded. Ten specimens were made and tested for each core material.

Diametral tensile strengths were determined in a manner similar to the compressive test. Specimens 6 mm in diameter and 2-mm thick were mounted diametrically between disks of blotting paper on the platens of universal testing machine. Load was plotted against time so that any measurable permanent deformation could be noted. Ten specimens were made and tested for each group. A three-point bending test was carried out using a universal testing machine to evaluate the flexural strength. The cross-head speed was set at 0.1 mm/min. The mean specimen dimensions were 25 × 2 × 2 mm. Ten samples were measured for each group.

Statistical analysis for the strength of core materials was performed, and the mean value with its standard deviation was calculated for each core material. Kruskal-Wallis test was performed to determine whether statistically significant differences (P < 0.05) existed among core materials.

 RESULTS



According to the results of factorial variance analysis done for compressive strength, dimetral tensile strength, and flexural strengths of core materials and the interactions between the factors were statistically significant.

Data were analyzed using Statistical Package for Social Sciences (SPSS) version 11.5 (SPSS Inc, Chicago IL). Descriptive statistics were calculated. Kruskal-Wallis test was applied to assess the difference between flexural, compressive, and diametral strength between groups. Using this method, variables selected will be those that show the significant difference at the 95% level (P < 0.05).

The compressive strength values for the materials were not found to be statistically significant. Diametral tensile strength of materials was found to be statistically significant with the values for ParaCore were significantly higher than those for all the other materials investigated. It was determined that amalgam is the weakest of all regarding tensile strength. Amalgam and P90 showed small changes compared with other materials. Significant differences were observed in the diametral tensile strength values for ParaCore and LuxaCore resin composite materials [Table 1].{Table 1}

Flexural strength values were significantly higher for P90 composite resin at humid temperature than those for all the materials tested with. Amalgam and ParaCore composite resin material showed the lowest flexural strength values compared with other materials.

 DISCUSSION



According to the results of the study, resin composite core build up materials showed better mechanical properties than silver amalgam core, which is similar to the results of study done by Bonilla et al.[22] This could be due to the micromechanical bonding (monoblock effect) of resins to the tooth structure and resin composites behaving like stress breakers as well as complete curing of material with dual cure technology. [23],[24],[25] Results of our study were consistent with the results of study done by Choi and others who found that some resin composites exhibited compressive strengths more than that of amalgam and could be used as alternatives to amalgam. [17] In our study, ParaCore composite resin material showed excellent physical properties because it is reinforced with glass fibers; it is a dual cure material that will ensure complete cure, thereby improve the strength of the material. The macroscopic size of the unidirectional fiber bundles used in fiber reinforces the resins and improves their mechanical properties. The presence of fibers affects the fracture process that results in interrupting crack growth progression and thus enhances the fracture toughness of the fiber-reinforced composite material. [14] The present study is in agreement with the study done by Peterson et al. [23]

LuxaCore showed comparative results with the ParaCore composites in all three properties, as both are dual cure materials. The nanotechnology used in LuxaCore dual eliminates particle agglomeration by incorporating a proprietary coating process during particle manufacture. LuxaCore dual (DMG) possesses strength, flexibility, and insulation properties similar to that of dentin, according to manufacturers. Type of fillers in LuxaCore is aluminoborosilicate glass, fumed silica, and titanium oxide, which could be the reason for their high strength. Similar results are found by Seung-Geun Ahn, and John A. Sorensen, in a study. [26]

In the present study, FiltekTM P90 (3M ESPE) composite resin showed the best flexural strength because of their the flexural fatigue limit is 80 MPa, indicating that under clinical conditions may likely to withstand mastication forces without fracturing even after many years in service. [21] In the present study, FiltekTM P90 composite resin was found to have lesser compressive strength compared with ParaCore and LuxaCore without statistical significant difference, whereas the diametral tensile strength was statistically low.

The results of our study indicate that, on the basis of their mechanical properties, dual cure core build up resin composites with nanofillers may be used as alternatives to amalgam core. When choosing the core material, the amount and mode of stress must be considered because it affects the stress transmission of the post. As the firmness increases, the stress goes more directly to the root and less to the post. Metal cores are known to cause great stress in the coronal part and to send the stress directly to the root. It is also important to choose a core that has similar physical properties with the post because of the favorable strong interface and lower risk of microleakage and failure.

Further studies concerning about fatigue load, insufficient adhesive strength between the resin cement and the crown, the effect of deformation of the resin core due to masticatory or shearing force on failure of glass fiber post are needed to be conducted.

 CONCLUSIONS



With the constraints of the test design, the following conclusions were drawn from this in vitro study:

1. Both dual cure composite materials with nanofillers were found superior to amalgam core.

2. The silorane-based material showed the highest flexural strength, but other mechanical properties were inferior to dual cure composite materials with nanofillers.

Referring to the values of maximum fracture load and mean compressive fracture load, dual cure resin composites have high values and are recommended as tooth-colored resin core build up materials.

References

1Current clinical trends in restoring the endodontically treated tooth. Highlights of a symposium. Toronto, Canada. February, 1988. J Clin Dent 1988;2:39-47.
2Combe EC, Shaglouf A. Mechanical properties of direct core build-up materials. Dent Mater 1999;15:158-65.
3Levartovsky S, Kuyinu E, Georgescu M, Goldstein GR. A comparison of the diametral tensile strength, the flexural strength and the compressive strength of two new core materials to a silver alloy reinforced glass-ionomer material. J Prosthet Dent 1994;72:481-5.
4Cho GC, Kaneko LM, Donovan TE, White SN. Diametral and compressive strength of dental core materials. J Prosthet Dent 1999;82:272-6.
5Huysmans MC, Van der Varst PG. Finite element analysis of quasistatic and fatigue faliure of post and cores. J Dent 1993;21:57-64.
6Huysmans MC, van der Varst PG. Mechanical longevity estimation model for post and core restorations. Dent Mater 1995;11:252-7.
7Saygili G, Sahmali S. Comparative study of the physical properties of core materials. Int J Periodontics Restorative Dent 2002;22:355-63.
8Vagra J, Matsumura H. Bonding of amalgam filling in tooth cavity with adhesive resin. Dent Mater J 1986;5:158-64.
9Staninec M. Retention of amalgam restorations: Undercuts verus bonding. Quintessence Int 1989;20:347-51.
10Ferrier S, Sekhon BS, Brunton PA. A study of the fracture resistance of nyyar cores of three restorative materials. Oper Dent 2008;33:305-11.
11Starr CB. Amalgam crown restoration for posterior pulpless teeth. J Prosthet Dent 1990;63:614-9.
12Bowen RL. Properties of silica reinforced polymer for dental restorations. J Am Dent Assoc 1963;66:57-64.
13Weathersby J, Xu S, Winkler M. AADR Chicago; 2001. J Dent Res 80.
14Post Paracore automix dual cure material, Coltene Whaledent, Switzerland, brochure.
15Nicoleta I, Hickel R. Macro, micro and nano mechanical investigations on silorane and methacrylate based composites. Dent Mater 2009;25:810-9.
16Uno S, Asmussen E. Effect on bonding of curing through dentin. Acta Odontol Scand 1991;49:317-20.
17Choi KK, Chodon JR. The efects of adhesive thickness on polymerization contraction stress of composite. J Dent Res 2000;79:812-7.
18Braga RR, Ferracane JL. Polymerization contraction stress in dual cure cements and its effect on interfacial integrity of bonded inlays. J Dent 2002;30:333-40.
19Ferracane JL. Developing a more complete understanding of stresses produced in dental composites during polymerization. Dent Mater 2005;21:36-42.
20Weinmann W, Thalacker C. Siloranes in dental composites. Dent Mater 2005;21:68-74.
21Vieback A, 3M ESPE AG, Seefeld, Germany. Compressive strength and flexural strength of Filtek P90 Study Booklet for Latin America/Asia Pacific-3M. http://www.multimedia.3m.com/mws/mediawebserver?mwsId...fn=p90...pdf. [Last accessed on 2014 Mar 09].
22Bonilla ED, Mardirossian G, Caputo AA. Fracture toughness of various core build-up materials. J Prosthodont 2000;9:14-8.
23Hornbrook DS, Hastings JH. Use of a bondable reinforcement fiber for post and core build-up in an endodontically treated tooth: Maximizing strength and aesthetics. Pract Periodontics Aesthet Dent 1995;7:33-42.
24Petersen RC. Discontinuous fiber-reinforced composites above critical length. J Dent Res 2005;84:365-70.
25Foxton RM, Nakajima M, Tagami J, Miura H. Adhesion to root canal dentine using one and two-step adhesives with dual-cure composite core materials. J Oral Rehabil 2005;32:97-104.
26Seung-Geun Ahn, John A. Sorensen. Comparison of mechanical properties of various post and core materials. J Korean Acad Prosthodont 2003;41.