ORIGINAL ARTICLE
Year : 2013  |  Volume : 16  |  Issue : 3  |  Page : 243-246

Effect of Ethylene diamine tetra acetic acid and sodium hypochlorite solution conditioning on microtensile bond strength of one-step self-etch adhesives


1 Dental Research Center, Department of Operative Dentistry, Dental School, Hamadan University of Medical Sciences, Hamadan, Iran
2 Department of Operative Dentistry, Dental School, International Branch of Shahid Beheshti Medical University, Tehran, Iran

Correspondence Address:
Zahra Khamverdi
Dental Research Center, Dental School, Hamadan University of Medical Sciences, Hamadan
Iran
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/0972-0707.111324

Rights and Permissions

Background: Attempts to improve bond strength of self-etch adhesives can enhance the durability of composite restorations. Aims: The aim of the present study was to evaluate the effect of collagen and smear layer removal with sodium hypochlorite solution (NaOCl) and EDTA on micro-tensile bond strength (μTBS) of self-etch adhesives to dentin. Settings and Design: It was an in-vitro study. Materials and Methods: Seventy-two teeth were divided into eight groups and their crowns were ground perpendicular to their long axis to expose dentin. The teeth were polished with silicon-carbide papers. The groups were treated as follows: No conditioning, 0.5-M EDTA conditioning, 2.5% NaOCl conditioning, NaOCl + EDTA conditioning. The surfaces were rinsed and blot-dried. Clearfil S3 and I-Bond were applied according to manufacturers' instructions and restored with Z100 composite. After 500 cycles of thermo-cycling between 5±C and 55±C, the samples were sectioned and tested for μTBS. Statistical Analysis: Data were analyzed by two-way ANOVA and Tukey-HSD test. Results: The highest μTBS was recorded with Clearfil S3 + NaOCl + EDTA, and the lowest was recorded with I-Bond without conditioning. μTBS in EDTA-and EDTA + NaOCl-treated groups was significantly higher than the control and NaOCl-conditioned groups. Conclusions: Application of EDTA or EDTA + NaOCl before one-step self-etch adhesives increased μTBS.


[FULL TEXT] [PDF]*
Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)
 

 Article Access Statistics
    Viewed1371    
    Printed35    
    Emailed0    
    PDF Downloaded132    
    Comments [Add]    

Recommend this journal