ORIGINAL ARTICLE
Year : 2011  |  Volume : 14  |  Issue : 3  |  Page : 277-281

Fracture resistance of endodontically treated premolars with direct composite restorations


Department of Operative Dentistry, School of Dentistry, Tehran Azad University of Medical Sciences, Tehran, Iran

Correspondence Address:
Maryam Moezizadeh
Department of Operative Dentistry, School of Dentistry, Shaheed Beheshti University of Medical Sciences, Tehran
Iran
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/0972-0707.85816

Rights and Permissions

Purpose: To determine the fatigue resistance and failure mode of endodontically treated premolars using direct composite resin restorations. Materials and Methods: Eighty-four human premolars were divided into seven groups of 12, prepared as follows: Intact teeth used in Group 1 as control, the second group covers the endodontically treated teeth, restored with direct onlays using Z250 composite resin, the next two groups (i.e. 3,4) were similar to the second group, but subjected to 1 and 2 million fatigue load cycles, respectively. Groups 5, 6, 7 were similar to groups 2, 3, 4, however, in these groups Tetric Ceram was used as the restorative material. All specimens were loaded using a Universal Testing Machine until fracture occurred. One-way Anova andTukey's HSD tests were used to analyze the data of onlay groups. Results: All specimens withstood the masticating simulation. The mean fracture strength for Goups 1 to 7 was: 1276.92, 1373.47, 1269/70, 486/35, 484/12, 1130/49, 1113/79 Newton, respectively. No statistically significant differences were found between the groups in fracture strength and failure mode. Conclusions: No statistically significant differences in fracture strength were found between sound teeth and composite onlays that were subjected to 1 and 2 million fatigue load cycles.


[FULL TEXT] [PDF]*
Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)
 

 Article Access Statistics
    Viewed2053    
    Printed109    
    Emailed0    
    PDF Downloaded191    
    Comments [Add]    
    Cited by others 2    

Recommend this journal